Robust epitaxial growth of two-dimensional heterostructures, multiheterostructures, and superlattices

We report a general synthetic strategy for highly robust growth of diverse lateral heterostructures, multiheterostructures, and superlattices from two-dimensional (2D) atomic crystals. A reverse flow during the temperature-swing stage in the sequential vapor deposition growth process allowed us to cool the existing 2D crystals to prevent undesired thermal degradation and uncontrolled homogeneous nucleation, thus enabling highly robust block-by-block epitaxial growth. Raman and photoluminescence